JIS G3131 Hot-Rolled Steel
|
Classification |
Spec |
Chemical Composition (%) |
Tensile Strength N/mm² |
Elongation (%) |
|
C |
Mn |
P |
S |
≥1.20mm to <1.60mm |
≥1.60mm to <2.00mm |
≥2.00mm to <2.50mm |
≥2.50mm to <3.20mm |
≥3.20mm to <4.00mm |
≥4.00mm |
|
Commercial Quality |
SPHC |
0.15max |
0.60max |
0.05max |
0.05max |
270min |
27min |
29min |
29min |
29min |
31min |
31min |
|
Drawing |
SPHD |
0.10max |
0.50max |
0.04max |
0.04max |
270min |
30min |
32min |
33min |
35min |
37min |
39min |
|
Deep Drawing |
SPHE |
0.10max |
0.50max |
0.03max |
0.04max |
270min |
31min |
33min |
35min |
37min |
39min |
41min |
|
ASTM Standard |
|
 |
|
Specification |
Type |
Chemical Composition(%) |
|
C |
Mn |
P |
S |
Al |
|
A569 (Commercial Quality) |
A |
0.10max |
0.60max |
0.03max |
0.035max |
- |
|
B |
0.02~0.15 |
|
C |
0.08max |
0.10max |
|
A622 (Drawing Quality, special killed) |
A |
0.08max |
0.50max |
0.02max |
0.03max |
0.01min |
|
B |
0.02~0.08 |
0.02min |
|
|
 Download Specifications in PDF |
|
|
|
|
|
|
|
|
|